I-Quartz Rod
Isicelo:
Ishishini leMetallological
Ishishini lokwakha
Ishishini leglasi
Inkcazo
Ubungakanani obuqhelekileyo
|
Uluhlu lwe-OD(mm) |
Unyamezelo lwe-OD(mm) |
I-ovality |
Ukuqubuda |
|
OD Ngaphantsi okanye ilingana no-5.0 |
±2.00%OD |
2.00% |
0.20% |
|
5.0＜OD＜10.0 |
±1.00%OD |
1.00% |
0.10% |
|
10.0＜OD＜20.0 |
±1.00%OD |
1.00% |
0.10% |
|
20.0＜OD＜30.0 |
±1.00%OD |
1.00% |
0.10% |
|
30.0＜OD＜50.0 |
±1.00%OD |
1.00% |
0.10% |
|
50.0＜OD＜100.0 |
±1.00%OD |
1.00% |
0.15% |
|
100.0＜OD＜160.0 |
±1.00%OD |
1.00% |
0.15% |
Umxholo wokungcola
|
Ikhowudi |
Iikhrayitheriya |
Al |
Ca |
Cr |
Cu |
Fe |
K |
|
PQ191E |
Isiqhelo |
13.0 |
0.50 |
<0.05 |
<0.05 |
0.10 |
0.10 |
|
Ubuninzi |
19.0 |
1.00 |
0.10 |
0.10 |
0.50 |
1.00 |
|
|
I-PQ191EH |
Isiqhelo |
8.0 |
0.60 |
<0.05 |
<0.01 |
0.10 |
0.10 |
|
Ubuninzi |
10.0 |
1.00 |
0.10 |
<0.01 |
0.50 |
0.50 |
|
|
Ikhowudi |
Iikhrayitheriya |
Li |
Mg |
Mnu |
N / A |
Ti |
Zr |
|
PQ191E |
Isiqhelo |
0.3 |
0.05 |
0.05 |
0.10 |
1.30 |
1.00 |
|
Ubuninzi |
1.00 |
0.20 |
0.20 |
1.00 |
2.00 |
2.00 |
|
|
I-PQ191EH |
Isiqhelo |
0.20 |
0.05 |
0.05 |
0.10 |
1.30 |
1.00 |
|
Ubuninzi |
0.50 |
0.20 |
0.20 |
0.50 |
2.00 |
2.00 |
Iipropati
- Customization Ukuguquguquka
- Phezulu - uQinisekiso loMgangatho
- Iindleko - Ukusebenza okusebenzayo
- Ukuhanjiswa okukhawulezayo nokuthembekileyo
IiNdawo zokuSebenza
- Ishishini lePetrokhemikhali
- Ishishini lezamayeza
- Ubunjineli bokuSingqongileyo
Iipropati
|
Iipropati Zomzimba |
Imilinganiselo |
|
Ubunyulu |
＞99.99% |
|
Ukuxinana |
2.2g/cm3 |
|
Ukungafihli |
＞90% |
|
Mohs Ubunzima |
5.5--6.5 |
|
Indawo yoTshintsho |
1280 idigri |
|
Inqaku lokuthambisa |
1750 idigri |
|
Inqaku le-Anealing |
1250 idigri |
|
Ubushushu obubodwa (20 - 350 isidanga ) |
670J/kg. isidanga |
|
I-Thermal Conductivity (20 degree) |
1.4W/m. isidanga |
|
Ukuhanjiswa kobushushu (w/mk, 1000 degree) |
1.0-1.2 |
|
Refractive Index |
1.4585 |
|
I-Coefficient yoKwandiswa kweThermal |
5.510 -7cm/cm. isidanga |
|
Kushushu - ubushushu bokusebenza |
1750--2050 idigri |
|
Ixesha elifutshane - loBubushushu beNkonzo |
1450 idigri |
|
Ixesha elide - loBubushushu beNkonzo |
I-1100 degree |
|
Iipropati zeMichiza |
Imilinganiselo |
|
Ukumelana ne-Acid |
I-Acid eyomeleleyo (ngaphandle kwe-HF), i-alkali eyomeleleyo, isisombululo se-organic |
|
Amaqondo obushushu aphezulu Ukumelana nokuCorrosion |
Egqwesileyo |
|
Isiqulatho seMetal yokungcola |
＜5 ppm |
|
Iipropati zoMbane |
Imilinganiselo |
|
Ukuxhathisa |
7107Ω.cm |
|
Ukomelela kweInsulation |
250~400Kv/cm |
|
Dielectric Constant |
3.7~3.9 |
|
I-Dielectric Absorption Coefficient |
＜410-4 |
|
I-Dielectric Loss Coefficient |
＜110-4 |
|
Iipropati zoomatshini |
Imilinganiselo |
|
Amandla acinezelayo |
1100MPa |
|
Ukugoba Amandla |
67MPa |
|
Tensile strength |
48MPa |
|
Umlinganiselo wePoisson |
0.14~0.17 |
|
Imodulus yolutsha |
72000MPa |
|
Shear Modulus |
31000MPa |
FAQ
Umbuzo: Ziziphi iidayimitha kunye nokunyamezela okukhoyo?
A: Uluhlu olusemgangathweni:
- Ububanzi: 1mm–150mm (±0.05mm)
- Ubude: ukuya kuthi ga kwi-2000mm (±1mm)
- Ubungakanani obulungiselelweyo obunokunyamezela okungqongqo (±0.01mm)
Umbuzo: Ngaba iintonga ze-quartz zinomatshini emva kokunikezelwa?
A: Ewe, sicebisa:
- Isixhobo sedayimani sokusika
- CO₂ laser drilling (for holes >0.5mm)
- Ukukhazimliswa komlilo ukwenzela unyango edge
Umbuzo: Ngaba iintonga zakho zequartz zifanelekile kwizikhokelo zokukhanya kwe-UV?
A: Ewe, nge:
- >90% transmission @185nm (UV grade)
- Ngokuzikhethela iindawo ezikhazimlisiweyo eziphezulu (Ra<1nm)
Umbuzo: Zipakishwa njani iintonga ukukhusela umonakalo?
A: Multi{0}}ukhuseleko lomaleko:
- Imikhono yePVC yomntu ngamnye
- Ugwebu{1}}olwahlulwe amakhreyithi omthi
- Ukufuma{1}}iingxowa ezingqina ukufuma (ukhetho lwenitrogen yokucocwa)
Iifayile ezishisayo: intonga yequartz, China abavelisi beentonga zequartz, ababoneleli, umzi-mveliso
Thumela u kuphanda
Unokuthanda